Use Of Ceramic Waste In Concrete

For each mix six cubes of size 100 mm six.

Use of ceramic waste in concrete.

Thus the current study focuses on the mechanical characterization of waste ceramic wall and floor tiles aggregate concrete. They have studied on the issues of environmental and economic concern had addressed by the use of waste glass as partial. The evaluation of ceramic waste for use as a replacement of cement material begins with the concrete testing. The physical and mechanical properties of the ceramic waste coarse aggregate and conventional crushed stone coarse aggregate were determined as per is 2386 part i viii 1963.

Concrete contains cement water fineaggregate coarse aggregate and grit. Ceramic wastes sourced from construction and demolition wastes were separated from other debris and crushed using a quarry metal hammer. Manufacturing of ceramic tiles require different raw material like clay potash dolomite feldspar talc and different chemicals like sodium silicate sodium tripoly. With the control concrete i e.

Ceramic tiles were sieved into fine and coarse aggregates in line with standards. Cwp is characterized by its chemical composition that is mainly composed of silica sio2 and alumina al2o3. 10 20 30 40 and 50 of the cement is replaced with ceramic waste the data from the ceramic waste is. The disposal of cwp in landfills will cause significant environmental problems i e soil air and groundwater pollution.

The ceramic aggregate used in this study wasrecycled from industrial ceramic tile waste in egypt. On the one side an economic advantage derived by cutting down on the use of high grade quarry aggregates and reducing distances travelled by the material. Ceramic wall tiles are used as building material in the field of construction. 0 15 20 25 30 and 35 using grade m 20 weight of concrete.

Abstract this paper presents the results of an experimental studyto investigate the potential of using recycled ceramic as aggregate in concrete. The global production of ceramic waste powder cwp which is produced during the final polishing process of ceramic tiles exceeds 22 billion tons. So what is done that the opc cement is replaced with the waste of ceramic powder consequently in various stages. The results indicate effectiveness of crushed glass waste and ceramic waste as partial replacement of conventional aggregate up to 40 percent without affecting the design strength.

To understand the workability of ceramic waste coarse aggregate concrete and conventional concrete slump test was conducted as per is 7320 1974.